Short Description

Model No.: 316L-Straight-Hex-Nipple-Male-NPT-25-150LBS

China Hex Nipple Manufacturer www.steeljrv.com offers 316L Straight Hex Nipple Male NPT, DN25, 150LBS.

Request a quote Share

Key Specifications / Features

Type: Straight Hex Nipple
Material: A182 F316L
PN: 150LBS
Thread: Male NPT
Size: 1 Inch (DN25)

Chemical Composition and Mechanical Property for 316L

Steel Grade

Chemical Composition

Mechanical Performance

C(Max)

Si(Max)

Mn(Max)

P(Max)

S(Max)

Ni

Cr

N(Max)

Mo

Tensile Strength
(Min)

Yield Strength
(Min)

Mpa

Mpa

316L

0.03

0.75

2.00

0.045

0.03

10.0–14.0

16.0–18.0

0.1

2.00–3.00

485

170

20170914204444 71332 - 316L Straight Hex Nipple Male NPT DN25 150LBS

Standard Pattern 

SIZE 1/8″ 1/4″ 3/8″ 1/2″ 3/4″ 1″ 1-1/4″ 1-1/2″ 2″ 2-1/2″ 3″ 4″
mm in mm in mm in mm in mm in mm in mm in mm in mm in mm in mm in mm in
W 5.7 0.22 6 0.24 6.1 0.24 7.6 0.3 8.4 0.33 8.3 0.33 10 0.39 10.2 0.4 10.6 0.42 13.1 0.52 13 0.51 14.5 0.57
H 12.2 0.48 13 0.51 13 0.51 17.2 0.68 17.6 0.69 20.4 0.8 20.8 0.82 20.7 0.81 22 0.87 25 0.98 27.5 1.08 30.3 1.19
S 13.3 0.52 15.2 0.6 18.5 0.73 23 0.91 29 1.14 35 1.38 44 1.73 50 1.97 62 2.44 78 3.07 91 3.58 117 4.61
L 30 1.18 32 1.26 32 1.26 42 1.65 43.5 1.71 49 1.93 51.5 2.03 51.5 2.03 54.5 2.15 63 2.48 68 2.68 75 2.95

Tolerance: +0.5mm(1/8″~2″)

+0.8mm(2-1/2″~4″)

Economic Pattern

SIZE 1/8″ 1/4″ 3/8″ 1/2″ 3/4″ 1″ 1-1/4″ 1-1/2″ 2″ 2-1/2″ 3″ 4″
mm in mm in mm in mm in mm in mm in mm in mm in mm in mm in mm in mm in
W 5.6 0.22 6 0.24 6 0.24 7.6 0.3 8.5 0.33 8 0.31 9.5 0.37 9.5 0.37 10.5 0.41 13 0.51 13 0.51 15 0.59
H 9 0.35 11 0.43 11 0.43 14 0.55 14 0.55 17.5 0.69 18 0.71 18.5 0.73 20 0.79 22.5 0.89 25 0.98 28 1.1
S 13 0.51 15 0.59 18 0.71 23 0.91 29 1.14 35 1.38 45 1.77 50 1.97 62 2.44 78 3.07 91 3.58 118 4.65
L 26 1.02 30 1.18 30 1.18 40 1.57 40.5 1.59 48 1.89 49.5 1.95 49.5 1.95 52.5 2.07 60 2.36 65 2.56 71 2.8

Tolerance: +0.5mm(1/8″~2″)

+0.8mm(2-1/2″~4″)

Request a quote

Subject:

Products Related to 316L Straight Hex Nipple Male NPT DN25 150LBS

  • No related articles